    DC53模具钢和LD模具钢的区别

    来源:https://www.jnqhmj.com/ 日期:2022-05-05 发布人:guanli


    Cr12是一款高碳高铬型莱氏体冷作模具钢,硬度高,可达HRC60,但脆性大,模具*易开裂;淬透性差,心部无法淬硬,热处理后变形量大。好处是便宜,其它性能跟DC53相比, 都是缺点。
    Cr12 is a high carbon and high chromium ledeburite cold working die steel with high hardness up to HRC60, but it is brittle and the die * is easy to crack; The hardenability is poor, the core cannot be hardened, and the deformation is large after heat treatment. The advantage is that it is cheap. Compared with DC53, other performances are disadvantages.
    DC53是一款抗崩裂性能好的冷作模具钢,硬度HRC60-62,耐磨性好,抗崩裂性能是SKD11的2倍,模具不会开裂;且淬透性好,心部硬度和表面硬度趋于一致。
    DC53 is a cold working die steel with good anti cracking performance, with hardness of hrc60-62 and good wear resistance. The anti cracking performance is twice that of SKD11, and the die will not crack; The hardenability is good, and the core hardness and surface hardness tend to be the same.
    主要表现在:
    It is mainly reflected in:
    1)DC53的抗崩裂性能比Cr12强很多倍,DC53做的冲压模具不易开裂,用Cr12做的冲压模具,开裂是必然现象。
    1) The anti cracking performance of DC53 is many times stronger than that of Cr12. The stamping die made of DC53 is not easy to crack. For the stamping die made of Cr12, cracking is an inevitable phenomenon.
    2)使用硬度不同,Cr12硬度一般是GRC55-58,硬度高了容易开裂;DC53的正常硬度HRC60-62
    2) The hardness of Cr12 is generally grc55-58, which is easy to crack when the hardness is high; Normal hardness of DC53 hrc60-62
    3)线切割开裂风险不一样,Cr12淬火加硬后,线切割要开裂,而DC53不会。
    3) The risk of wire cutting cracking is different. After quenching and hardening of Cr12, wire cutting will crack, while DC53 will not.
    4)淬硬性不同,Cr12心部无法淬硬,而DC53的表面硬度和心部硬度趋于一致。
    4) With different hardenability, the core of Cr12 cannot be hardened, while the surface hardness and core hardness of DC53 tend to be the same.
    5)使用场合不同,Cr12用于仅要求耐磨,没有冲击的模具工况,模具结构简单;DC53主要用于要求抗冲击韧性的场合,且能保证很好的耐磨性。DC53主要用于模具制造。
    5) Different application occasions, Cr12 is used for die working conditions requiring only wear resistance and no impact, and the die structure is simple; DC53 is mainly used in occasions requiring impact toughness, and can ensure good wear resistance. DC53 is mainly used for mold manufacturing.
    6)售价不同,Cr12的好处是便宜,DC53售价比Cr12高好几倍。
    6) The price is different. The advantage of Cr12 is that it is cheap. The price of DC53 is several times higher than that of Cr12.
    如果用一句话表达DC53和Cr12的区别,可以用新旧社会两重天来形容也不为过。
    If the difference between DC53 and Cr12 is expressed in one sentence, it can be described as the dual heaven of the old and new society.
    有人问:LD模具钢和DC53模具钢哪个好?
    Someone asked: which is better, LD die steel or DC53 die steel?
    LD的冷镦模具钢,DC53是抗崩裂性能好的冷作模具钢。他们的使用硬度都是HRC60-62,耐磨性相当,但DC53的抗崩裂性能比LD好。
    LD cold heading die steel, DC53 is a cold working die steel with good cracking resistance. Their use hardness is hrc60-62, and the wear resistance is equivalent, but the cracking resistance of DC53 is better than that of LD.
    表示抗崩裂性能的技术参数是冲击功值,DC53硬度HRC61的冲击功值是72焦耳,LD硬度HRC54的冲击功值是18.4焦耳(冲击功数值和式样尺寸大小有关,不是值),由此表明,LD的抗冲击能力差于DC53。
    The technical parameter indicating the anti cracking performance is the impact energy value, the impact energy value of DC53 hardness HRC61 is 72 joules, and the impact energy value of LD hardness hrc54 is 18.4 joules (the impact energy value is related to the size of the pattern, not the value), which shows that the impact resistance of LD is worse than that of DC53.
    还有LD模具钢的淬火温度高达1100℃,DC53淬火温度1020-1050℃;LD的热处理工艺不好把控,热处理出来的材料性能不稳定;而DC53的热处理工艺更加容易把控,这对工业生产有好处。
    In addition, the quenching temperature of LD die steel is as high as 1100 ℃, and the quenching temperature of DC53 is 1020-1050 ℃; The heat treatment process of LD is not easy to control, and the properties of materials after heat treatment are unstable; The heat treatment process of DC53 is easier to control, which is beneficial to industrial production.
    以上就是为大家介绍的有关冷作模具钢的详细介绍,希望对您有所帮助.如果您有什么疑问的话,欢迎联系我们.我们将以的态度,为您提供服务https://www.jnqhmj.com
    The above is the detailed introduction of cold working die steel for you. I hope it will be helpful to you If you have any questions, please contact us We will provide service for you with our attitude https://www.jnqhmj.com